Physical Properties
|
|
|
|
|
|
Density
|
1.85 g/cc minimum
|
|
Wear Rate
|
0. 0054 in3/hp-hr
|
|
Ultimate
tensile strength
|
3,100 psi
|
|
Modulus x 106
|
2.10 psi
|
|
Elongation
|
0.16%
|
|
Ultimate
flexural strength
|
5,400 psi
|
|
Modulus x 106
|
0.06 psi
|
|
Ultimate
compressive strength
|
12,000 psi
|
|
Ultimate
shear strength
|
5,700 psi
|
|
Conductivity
|
2.97 BTU-in/hr/ft2/°F
|
|
(All physical
properties shown above are all mean values)
|
|
|
|
|
|
Technical
Data
|
|
|
μ for design
purposes :
|
|
|
Normal
|
0.52
|
|
Hot
|
0.51
|
|
@204°C
|
0.52
|
|
Static @ 93°C
|
0.61
|
|
Static @
204°C
|
0.5
|
|
|
|
|
Recommended Operating Range
|
|
|
|
|
Maximum unit
pressure
|
250
|
|
Max. rubbing
speed
|
25 m/s (82 ft/s)
|
|
Min.
temperature
|
-23°C
|
|
Max.
continuous temperature
|
288°C
|
|
Max.
intermittent temperature
|
343°C
|
|
|
|
|
Mating
Surface
|
|
|
|
|
|
A good quality, fine grained, pearlitic cast iron or cold rolled
steel with a Brinellhardness of 180. Cast steels are notrecommended.
|
|
|
|
|
Availability
|
|
|
|
|
|
Sheet size 711mm x 914mm x 4.8mm upto 38mm thick Special shapes
and discson request.
|